Is zirconium nitride harmful to human body?

What's ZrN powder?

Zirconium-nitride =105.2, density 7.99g/cm3, and is a light yellow powder. ZrN has high chemical stability and a low decomposition temperature, making it a tough refractory material. This makes ZrN resistant to high temperatures, corrosion and wear. ZrN is an excellent high-temperature structure material, superhard tool and surface protector material. ZrN thin film is a light golden colour with low brightness. It is ideal for areas where titanium dioxide isn't suitable for coating. ZrN that has been grown via physical vapor deposit (PVD), is light golden and similar to elemental. ZrN's room temperature resistivity is 12.0mO*cm. It has a temperature coefficient of resistance of 5.6*10-8O*cm/K. It also has superconducting transitiontemperature of 10.4K. And the relaxation lattice parameter of 0.4575nm. ZrN, single crystal, has a hardness of 22.7+-1.7 GPa. The elastic modulus is 450 GPa.

Zirconium nitride is hard (15 GPa), 10, has a high melting point (32980+-50degC), excellent thermal conductivity (45-50W/mK), low resistance (45-50W/mK), good wear resistance, and high corrosion resistance. It is a popular choice for coatings of thermal barriers, mold settings for material process and diffusion barriers.

1. This material is widely used for powder metallurgy and fine ceramic raw material powder. It can also be used to conductive materials and decorative material. Good conductivity makes it suitable for use as a conductive material, such as in the manufacture of electrodes or electrical contacts during molten salt electrolysis. This material can be added to any hard tool.

2. It is used as powder metallurgy or fine ceramic raw material powder.

A variety of methods are used to synthesize zirconium nutride powder. These include direct nitridation Zr with nitrogen, high energy reactive ball milling, microwave plasma, and aluminum reduction.

1. Direct nitriding (direct nitriding) of metal zirconium, and nitrogen at temperatures of 1100-1200degC

Zirconium-tetrachloride is first formed an adduct in ammonia. Next, it's heated to 750C to become zirconium pentaride (Zr3N4). It then gets heated to 1200C to make zirconium nutride (ZrN). Ammonia can react above 1000 degrees Celsius in the presence sulfuric acid to make zirconium nutride.

There are many variables that influence the ZrN powder's market value. The market price of ZrN powder is changing rapidly at the moment. You can contact us anytime if you require it.

Mis-asia (aka. Mis-asia Technology Co. Ltd. (aka. Our company currently has a number of powder material products. You can also order OEM. Please email us or click the required products to send an inquiry if ZrN Powder is what you're looking for.