Role of Copper Oxides in Contact Killing of Bacteria


The potential of metallic copper as an intrinsically antibacterial material is gaining increasing attention in the face of the growing antibiotic resistance of bacteria. However, the mechanism of the so-called "contact killing" of bacteria by copper surfaces is poorly understood and requires further investigation. In particular, the influences of bacteria–metal interaction, media composition, and copper surface chemistry on contact killing are not fully understood. In this study, copper oxide formation on copper during standard antimicrobial testing was measured in situ by spectroscopic ellipsometry. In parallel, contact killing under these conditions was assessed with bacteria in phosphate-buffered saline (PBS) or Tris-Cl. For comparison, defined Cu2O and CuO layers were thermally generated and characterized by grazing incidence X-ray diffraction. The antibacterial properties of these copper oxides were tested under the conditions used above. Finally, copper ion release was recorded for both buffer systems by inductively coupled plasma atomic absorption spectroscopy, and exposed copper samples were analyzed for topographical surface alterations. It was found that there was a fairly even growth of CuO under wet plating conditions, reaching 4–10 nm in 300 min, but no measurable Cu2O was formed during this time. CuO was found to significantly inhibit contact killing, compared to pure copper.

In contrast, thermally generated Cu2O was essential as effective in contact killing as pure copper. Copper ion release from the different surfaces roughly correlated with their antibacterial efficacy and was highest for pure copper, followed by Cu2O and CuO. Tris-Cl induced a 10–50-fold faster copper ion release compared to PBS. Since the Cu2O that primarily forms on copper under ambient conditions is as active in contact killing as pure copper, antimicrobial objects will retain their antimicrobial properties even after oxide formation. If you are looking for high quality, high purity, and cost-effective Copper oxide, or if you require the latest price, please email contact mis-asia.

Inquiry us

Our Latest Products

Factory 3-5nm Nanodiamond Powder CAS 7782-40-3

Brief Introduction of Nanodiamond PowderProduct name: Nanodiamond PowderFormular: C Product NameNanodiamond PowderPurity 99%Particle Size3-5nmAnalysis ResultChemical CompositionAnalysis (%)Al0.0046%Co0.007%Si0.079%Na0.002%K0.00015%Ca0.003%Mg0.00058%...…

CAS No. 557-05-1 40% Water-based Zinc Stearate Zinc Stearate Emulsion

Product DescriptionProduct Description Description of zinc stearate emulsionZinc stearate emulsion is easy to disperse in water, has ultra-fineness, good dispersion compatibility. Zinc stearate emulsion has the characteristics of lubricating and deli...…

China factory cheapest price lightweight concrete wall panel making machine large hydraulic cement foaming machine equipment

Product performance of TR-40 Cement Foaming Machine1. The shell is made of high-strength precision thickened steel plate, painted twice, which is durable.2. The slurry output is uniform and stable, the density of the foam concrete finished product i...…

0086-0379-64280201 skype whatsapp