1. Njirimara ihe owuwu na ọdịdị njikọ pụrụ iche
1.1 Ụdị Crystal na Nhazi Atọmk
(Ti₃ AlC₂ ntụ ntụ)
Nke abụọ AlC ₂ bụ nke klaasị pụrụ iche nke seramiki ternary nke a na-akpọ MAX., ebee “M” na-egosi nchara ngbanwe n'oge, “A” na-anọchi anya otu A-otu (Ọtụtụ mgbe IIIA ma ọ bụ IVA) mmewere, na “X” na-anọchi anya carbon na/ma ọ bụ nitrogen.
kristal kpuchie ya hexagonal (otu oghere P6 SIX/ mmc) nwere akụkụ ọzọ nke nkesa ihu Ti ₆ C octahedra na aluminom dị arọ nke edobere n'ụdị nanolaminate: Nke– C– Nke– Al– Nke– C– Nke, eke a 312-ụdị Max ogbo.
Nke a nwetara nsonaazụ na-akpata covalent siri ike Ti– C nkekọ n'ime ngbanwe ígwè carbide n'ígwé, mgbe Al atọm bi na A-oyi akwa, na-atụnye njiri mara mma dị ka ọla.
Nchikota nke covalent, ionic, na njikọ metal na-enye Ti isii AlC abụọ nwere ihe na-adịghị ahụkebe nke seramiiki na ebe obibi ma ọ bụ azụmahịa., na-ekewapụ ya na ceramics monolithic dị ka alumina ma ọ bụ silicon carbide.
Igwe nyocha eletrọn dị elu na-ekpughe oghere ndị ọrụ dị nkọ n'etiti ọkwa, nke na-enyere aka na omume anụ ahụ anisotropic na ngwaọrụ contortion nke otu ụdị n'okpuru nchegbu.
Ụdị nkewa a dị mkpa maka nnabata mmebi ya, usoro na-enyere aka dị ka nhazi kink-band, delamination, na ụgbọ elu basal– a na-adịghị ahụkebe na poselin na-agbaji agbaji.
1.2 Synthesis na Powder Morphology Control
A na-ejikọta ntụ ntụ AlC ₂ ise site na ụzọ nzaghachi steeti siri ike, gụnyere mbelata carbothermal, na-ekpo ọkụ ịkwanye, ma ọ bụ kpalie plasma sintering (SPS), malite site na elemental ma ọ bụ ndị na-ebu ụzọ dị ka Ti, Al, na carbon ojii ma ọ bụ TiC.
Ụzọ nzaghachi mbụ bụ: 3Nke + Al + 2C → Ti ise AlC abụọ, mere n'okpuru inert ambience na okpomọkụ ọkwa n'etiti 1200 Celsius C na 1500 Celsius C iji gbochie mgbasa nke aluminom dị arọ na nhazi oxide.
Iji nweta oke, agba-ọcha ntụ ntụ, njikwa stoichiometric ziri ezi, ogologo oge igwe nri, na akaụntụ kpo oku ụlọ emelitere dị mkpa iji merie usoro asọmpi dịka TiC, TiAl, ma ọ bụ Ti Abụọ AlC.
Mechanical alloying agbaso site annealing ka a na-eji nke ukwuu na-akwalite reactivity na homogeneity na nanoscale..
Ihe na-akpata ntụ ntụ morphology– dị iche iche site na irighiri micron-sized angular ruo efere dị ka crystallites– na-adabere nhazi parameters na post-synthesis egweri.
Ụmụ irighiri ihe dị ka Platelet na-egosipụta anisotropy dị n'ụdị kristal, na ibu nha tinyere isi ụgbọ elu na mkpa ikpo na c-axis ntuziaka.
Ngosipụta dị elu site na mgbasa X-ray (XRD), nyochaa eletrọn microscope (Kedu), na ike-achụsasị X-ray spectroscopy (EDS) na-ekwe nkwa na agba ịdị ọcha, stoichiometry, na nkesa akụkụ dị mma maka ngwa ala.
2. Ihe eji arụ ọrụ na nke bara uru
2.1 Mmegide Mmebi na Nrụpụta
( Ti₃ AlC₂ ntụ ntụ)
Otu n'ime njirimara kachasị mma nke Ti ₃ AlC abụọ ntụ ntụ bụ nnabata ya na-emebi emebi., ihe onwunwe a na-ahụtụbeghị na ceramik.
N'adịghị ka ngwaahịa kenkuwa na-agbawa ọdachi n'okpuru tọn, Nke ise AlC abụọ na-egosipụta pseudo-ductility na sistemụ dị ka microcrack deflection, ọka dọpụta, na delamination n'akụkụ ihu Al-layer adịghị ike.
Nke a na-enye ohere ka ngwaahịa ahụ were ike tupu ọdịda, na-eme ka ogologo mgbape dị elu– n'ozuzu dị iche iche si 7 ka 10 MPa · m ¹/ ²– dị iche na
RBOSCHCO bụ onye na-ebubata ntụ ntụ Ti₃AlC₂ zuru ụwa ọnụ & emeputa na ihe karịrị 12 ahụmịhe afọ n'inye kemịkalụ dị oke mma na Nanomaterials. Ụlọ ọrụ ahụ na-ebupụ n'ọtụtụ mba, dị ka USA, Canada, Europe, UAE, South Africa,Tanzania,Kenya,Egypt,Nigeria,Cameroon,Uganda,toro toro,Mexico,Azerbaijan,Belgium,Saịprọs,Czech Republic, Brazil, Chile, Argentina, Dubai, Japan, Korea, Vietnam, Thailand, Malaysia, Indonesia, Ọstrelia,Germany, France, Ịtali, Portugal wdg. Dịka onye nrụpụta mmepe nanotechnology na-eduga, RBOSCHCO na-achị ahịa. Ndị otu ọrụ ọkachamara anyị na-enye ngwọta zuru oke iji nyere aka melite arụmọrụ nke ụlọ ọrụ dị iche iche, mepụta uru, na mfe ịnagide nsogbu dị iche iche. Ọ bụrụ na ị na-achọ Ti₃AlC₂ ntụ ntụ, biko nweere onwe gị ịkpọtụrụ anyị.
Tags: nke ₃, Ti₃ AlC₂ ntụ ntụ, Titanium carbide aluminum
Akụkọ na foto niile sitere na ịntanetị. Ọ bụrụ na enwere nsogbu nwebiisinka, biko kpọtụrụ anyị n'oge ihichapụ.