What’s ZrC powder exactly?
Zirconium carbid is an extremely hard material that has high melting points and good high-temperature resistance. You can use them to create alloy steel, and as solid fuel in rocket engines. This is also the raw material used to make zirconium metal or zirconium trioxide, as well as fine ceramic materials.
This material has a strong ZrC-C covalent bond which gives it a high melting temperature (3530degC), high module (440 GPa), hardness (25 GPa). ZrC’s density is 6.73g/cm3 lower than that of other carbides, such as TaC (14.75 g/cm3) or WC (15.8g/cm3). ZrC may be used for supersonic or rocket-hyper jet aircraft.
Method of production for zirconium carbonide
Both technetium oxide (or charcoal) are the raw materials. They are combined, put in a graphitecrucible to carbonize, heated to 2400 under hydrogen atmosphere and then reacted to produce zirconium caride. Mixing zirconia oxide and carbon black is also possible. They can be molded under pressure and heated to 1800 in an Induction Heating graphite Crucible. Once the hydrogen atmosphere has passed, they are added to Iy2% carbon noir and annealed at 1600 1900 in vacuum to make zirconium caride. You can also mix zirconium dioxide and magnesium, then heat to 750 and pickle with hydrochloric acids to extract byproducts.
Chemical vapor deposit is another method of manufacturing. The process involves heating the zirconium sponge, and decomposing any halide gases. The preparation of composite materials is one way to increase the resistance to oxidation. ZrC/ZrB2 is the preferred composite material. These composite materials are capable of working at temperatures above 1800°C. This situation can be improved by using another material, like TRISO fuel particle as a barrier.
Properties of chemicals
ZrC powder
Zirconium carbonide is a cubic, shiny and gray crystalline powder. Lattice constant. 1 0. 46983nm. Melting point 3532. Boiling point 5100. Relative density 6. 73. Mohs hardness 89, microhardness 2700kg/mm. The elastic modulus of 3. 48x10sN/mm2, thermal expansion coefficient 6. The heat of formation for 73×10-e/K is-196. 8kj/mol specific heat potential is 37. 8J/mol (mol-K), and resistance is 42u cm. Hydrochloric acid is insoluble. It dissolves in hydrofluoric, nitric, and hydrofluoric acids. However, it can be soluble or insoluble in hot sulfuric acid with hydrogen peroxide. The chemical reaction with chlorine can cause zirconium dioxide to be formed at higher temperatures.
ZrC powder’s price
There are several factors that influence the ZrC Powder market price. The market price of ZrC powder is changing rapidly at the moment. You can contact us anytime if you require it.
ZrC Powder Supplier
Mis-asia (aka. Mis-asia Technology Co. Ltd. (aka. Our company currently has a number of powder material products. You can also order OEM. Please email us or click the required products to send an inquiry.