What is WS2 powder?
Tungsten disulfide is an inorganic compound with the formula WS2 and molecular weight 247.97.
Gray with the metallic luster of fine crystals or powder, belonging to the hexagonal crystal system, semiconductor, and diamagnetic. The natural mineral is scheelite. Layered structure, easy to dissociate, similar to graphite lubrication properties.Used as a lubricant, as in aerosols.

Tungsten Disulfide WS2 Powder CAS 12138-09-9

WS2 powder physical properties
Tungsten disulfide is a compound of tungsten and sulfur, chemical formula WS2, molecular weight 247.97, the state of black gray powder, as dark gray hexane crystalline is solid. The relative density is 7.510.
Slightly soluble in cold water, soluble in hot water.Insoluble in hydrochloric acid and alkali (except concentrated nitric acid and hydrofluoric acid).Soluble in molten alkali, insoluble in alcohol.The density of 7.6 g · cm – 3. It has reducibility, can react with hot concentrated sulfuric acid, nitric acid, aqua regia, and other strong oxidants, and can be converted into WO3 when heated in air or oxygen. When heated to 1250℃ in a vacuum, it is decomposed into tungsten and sulfur. In a dry pure nitrogen stream, the mixture of tungsten trisulfide and sulfur is co-headed to 900℃ to sublimate the excess sulfur, and the residue is tungsten disulfide.
WS2 powder preparation methods
1. Roasting decomposition method:
Tungstic acid and ammonia reacted at 57 ~ 60℃ for 3h, and the natural precipitation was more than 16h. The ammonium tungstate was then reacted with hydrogen sulfide gas to produce ammonium tetrathiotungstate, which was decomposed into tungsten disulfide after roasting at a high temperature.
H2WO4 nh3 · H2O + 2 – (NH4) 2 wo4 + 2 H2O
(NH4) 2 wo4 + 4 h2s and (NH4) 2 ws4 + 4 h2o
2 (NH4) 2 ws4 o2 – > ws2 2 + 4 + 3 nh3 + 2 s + 2 so2 + H2O
2. Tungsten reacts very slowly with liquid sulfur.WS2 can be formed by sulfur-passing vapor from red-hot tungsten.WS2 can be formed when tungsten is mixed with Stoic thiowa and reacted at 800℃ for 24h in nitrogen atmosphere. If reacted at 6MPa and 1800℃, orthonormal WS2 can be formed.
3, with ammonium tetrathiotungstate as raw material, under the condition of air isolation, heating decomposition of ammonium tetrathiotungstate, heating at a temperature gradient of 100~200℃/ hour from room temperature to 700~1200℃, and this temperature for 24~48 hours, and then at a temperature gradient of 30~110℃/ hour to room temperature, discharge crushing.
The preparation method of ultrafine scaly crystal tungsten disulfide used for lubricant has simple equipment, no pollution to the environment, safe and reliable operation, and can produce high purity ultrafine tungsten disulfide with stable quality and hexagonal crystal structure.
WS2 powder Supplier
TRUNNANO (aka. Luoyang Tongrun Nano Technology Co. Ltd.) is a trusted global chemical material supplier & manufacturer with over 12 years of experience in providing super high-quality chemicals and Nanomaterials. Currently, our company has successfully developed a series of materials. The WS2 powder produced by our company has high purity, fine particle size, and impurity content. Send us an email or click on the needed products to send an inquiry.