1. Ohun elo Pataki ati Microstructural Ìfilélẹ
1.1 Ṣiṣe-soke ati Crystallographic iduroṣinṣin ti Alumina
(Alumina seramiki nozzles)
Alumina (Al ₂ O MEJI), paapa ni awọn oniwe-alpha alakoso, jẹ seramiki ti o ni oxidized patapata pẹlu iru corundum-iru hexagonal isunmọ, pese o lapẹẹrẹ gbona iduroṣinṣin, ailagbara kemikali, ati agbara ẹrọ ni awọn iwọn otutu ti o dide.
Alumina ti o ga julọ (deede 95– 99.9% Al ₂ O MEFA) jẹ ayanfẹ fun awọn ohun elo nozzle bi abajade ti akoonu idoti kekere rẹ, eyiti o dinku alaala ọkà ti o ni irẹwẹsi ati ilọsiwaju resistance si igbona ati ibajẹ kemikali.
Awọn microstructure, pẹlu itanran, equiaxed oka, ti wa ni atunse nigba sintering lati din porosity ati lilo ti o dara ju sisanra, taara ni ipa lori resistance ogbara nozzle ati iduroṣinṣin igbekalẹ labẹ ṣiṣan omi iyara-giga.
Awọn eroja bii MgO ni igbagbogbo gbekalẹ ni itọpa lapapọ lati ṣe idiwọ idagbasoke irugbin dani jakejado sisọ., ṣiṣe awọn ẹya microstructure aṣọ ti o ṣe atilẹyin pípẹ iyege.
1.2 Mechanical ati Gbona Properties Ti o yẹ si Nozzle Ṣiṣe
Awọn ohun elo alumina ṣe afihan iduroṣinṣin Vickers ti o kọja 1800 HV, ṣiṣe wọn ni sooro pupọ si yiya ti o ni inira lati awọn ṣiṣan ti o ni erupẹ, ẹya pataki ninu awọn ohun elo bii sandblasting ati gige omijet ti ko dun.
Pẹlu agbara ti o rọ ti 300– 500 MPa ati ki o kan compressive toughness lori 2 GPA, alumina nozzles ṣe aabo aabo onisẹpo labẹ ilana titẹ-giga, maa orisirisi lati 100 si 400 MPa ni awọn ọna ṣiṣe ile-iṣẹ.
Gbona, alumina da duro awọn oniwe-darí ile bi Elo bi 1600 ° C, pẹlu kan din ku gbona imugboroosi olùsọdipúpọ (~ 8 × 10 ⁻ / K) ti o pese atako resistance to gbona mọnamọna– pataki nigbati o ba tẹriba si awọn iyatọ iwọn otutu ni iyara jakejado ibẹrẹ tabi awọn akoko tiipa.
Awọn oniwe-gbona elekitiriki (~ 30 W/m · K) O to lati tu ooru agbegbe kuro lai fa awọn oke gbigbona ti o le ja si pipin, stabilizing idabobo ati ki o gbona isakoso ibeere.
2. Awọn ilana iṣelọpọ ati Ipeye Jiometirika
2.1 Apẹrẹ ati Awọn ọna Sintering fun iṣelọpọ Nozzle
Isejade ti alumina seramiki nozzles bẹrẹ pẹlu ga-mimọ lulú alumina, eyi ti o ti refaini ọtun sinu kan alawọ ewe ara ṣiṣe awọn lilo ti awọn ọna bi itura isostatic titẹ (CIP), abẹrẹ igbáti, tabi extrusion, da lori geometry ti o fẹ ati iwọn ti a ṣeto.
( Alumina seramiki nozzles)
Titẹ isostatic tutu nlo aapọn aṣọ lati gbogbo awọn ilana, ti o npese sisan iwuwo aṣọ kan ṣe pataki fun idinku awọn abawọn lakoko sisọ.
Iyipada abẹrẹ jẹ lilo fun awọn apẹrẹ nozzle eka pẹlu awọn tapers inu ati awọn orifices nla, muu ga onisẹpo yiye ati reproducibility ni ibi-gbóògì.
Lẹhin apẹrẹ, awọn iwapọ alawọ ewe ṣe itọju itọju igbona ipele meji: debinding lati se imukuro Organic binders ati sintering ni awọn iwọn otutu laarin 1500 ° C ati 1650 ° C lati ṣaṣeyọri sisanra imọ-jinlẹ nipasẹ itankale ipo-ipinle.
Iṣakoso gangan ti agbegbe sintering ati awọn idiyele alapapo / itutu agbaiye jẹ pataki lati daabobo lodi si titẹ, fifọ, tabi ọkà coarsening ti o le ewu nozzle iṣẹ.
2.2 Ṣiṣe ẹrọ, Sprucing Up, ati Iṣakoso Didara
Post-sintering, alumina nozzles nigbagbogbo nilo ẹrọ ṣiṣe deede lati ni awọn resistance to muna, ni pataki ni agbegbe orifice nibiti awọn abuda ṣiṣan jẹ ifarabalẹ julọ si ipari agbegbe ati geometry.
Lilọ Diamond ati fifọ ni a lo lati ṣatunṣe inu ati awọn agbegbe dada ita, iyọrisi dada roughness iye akojọ si isalẹ 0.1 µm, eyi ti o dinku resistance resistance ati yago fun ikojọpọ bit.
Orifice naa, commonly orisirisi lati 0.3 si 3.0 mm ni iwọn, ni lati wa laisi micro-cracks ati chamfers lati rii daju pe iṣan laminar ati awọn ilana sokiri deede.
Awọn ọna idanwo ti kii ṣe iparun gẹgẹbi airi opiti, Ayẹwo X-ray, ati awọn idanwo gigun keke titẹ ti wa ni iṣẹ lati rii daju iduroṣinṣin ti ayaworan ati iṣọkan iṣẹ ṣiṣe ṣaaju imuṣiṣẹ.
Aṣa-ṣe geometry, ti o wa ninu convergent-divergent (lati Laval) awọn profaili fun supersonic san tabi olona-iho orisirisi fun atele sokiri ilana, ti wa ni iṣelọpọ ni pataki nipa lilo ohun elo tuntun ati apẹrẹ iranlọwọ kọnputa (CAD)-ìṣó gbóògì.
3. Awọn anfani Iṣeṣe Lori Awọn Ohun elo Nozzle Yiyan
3.1 Superior Disintegration ati Ipata Resistance
Ni idakeji si ti fadaka (f.eks., tungsten carbide, irin ti ko njepata) tabi polima nozzles, alumina ṣe afihan resistance ti o tobi pupọ si yiya abrasive, paapa ni awọn agbegbe pẹlu yanrin yanrin, garnet, tabi awọn oriṣiriṣi awọn abrasives lile miiran ti a lo ni igbaradi dada ati gige.
Awọn nozzles irin n bajẹ ni kiakia nitori ti micro-fracturing ati abuku ṣiṣu, nilo aropo ibakan, lakoko ti awọn nozzles alumina le ṣiṣe ni 3– 5 igba Elo to gun, bosipo dindinku downtime ati iṣẹ-owo.
Ni afikun, alumina jẹ inert si ọpọlọpọ awọn acids, atacid, ati olomi, ṣiṣe awọn ti o yẹ fun kemikali splashing, etching, ati awọn ilana mimọ nibiti awọn eroja irin yoo ṣe ipata tabi ṣe akoran omi.
Aabo kemikali yii jẹ pataki ni iṣelọpọ semikondokito, elegbogi processing, ati ounje-ite ohun elo nilo ga funfun.
3.2 Gbona ati Electrical idabobo Properties
Alumina ká ga itanna resistivity (> 10 ¹⁴ Ω · sẹntimita) jẹ ki o dara fun lilo ninu awọn ọna ibora fun sokiri electrostatic, nibiti o ti yago fun jijo idiyele ati ṣe iṣeduro atomization kikun aṣọ.
Agbara idabobo igbona rẹ ngbanilaaye ilana ailewu ni awọn oju-aye fifa iwọn otutu giga, gẹgẹbi ina splashing tabi gbona ṣiṣe itọju, laisi gbigbe ooru si awọn eroja aala.
Ko dabi awọn irin, alumina ko ṣe mu ifasẹ pq ti a ko fẹ ninu awọn ṣiṣan omi ti o ni idahun, titọju awọn iyege ti elege solusan.
4. Awọn ohun elo Iṣẹ ati Ipa Imọ-ẹrọ
4.1 Awọn iṣẹ ni Abrasive Jet Machining ati dada itọju
Awọn nozzles seramiki alumina ṣe pataki ni awọn eto ibudanu inira fun yiyọ ipata, kun yiyọ, ati dada agbegbe texturing ni auto, ofurufu, ati awọn apa ile.
Agbara wọn lati tọju iwọn ila opin orifice deede lori lilo ti o gbooro sii rii daju pe oṣuwọn inira deede ati igun ipa, taara ipa dada agbegbe pari oke didara ati ilana repeatability.
Ni abrasive waterjet gige, alumina fifokansi tubes asiwaju awọn ga-titẹ omi-abrasive mix, diduro lodi si awọn ipa abrasive ti yoo yara bajẹ awọn ọja rirọ.
4.2 Lo ninu Iṣẹ iṣelọpọ Fikun, Sokiri Bo, ati iṣakoso omi
Ni gbona sokiri awọn ọna šiše, gẹgẹ bi awọn pilasima ati ina splashing, alumina nozzles taara awọn ṣiṣan gaasi iwọn otutu giga ati awọn patikulu didà sori awọn sobusitireti, nini lati igbona mọnamọna gbona wọn ati aabo onisẹpo.
Wọn ti wa ni bakanna ni oojọ ti ni deede sokiri nozzles fun ogbin kemikali, inkjet awọn ọna šiše, ati gaasi atomization, ibi ti yiya resistance idaniloju gun-pípẹ ohun elo konge.
Ni 3D titẹ sita, paapa ni binder jetting ati ọja extrusion, alumina nozzles pese awọn lulú nla tabi awọn lẹẹ viscous pẹlu idinamọ kekere tabi wọ.
Awọn ohun elo ti n yọ jade ni awọn ọna ṣiṣe microfluidic ati awọn ẹrọ lab-on-a-chip, ibi ti miniaturized alumina awọn ẹya ara lo sturdiness ati biocompatibility.
Ni atunṣe, alumina seramiki nozzles duro fun ọna agbekọja pataki ti imọ-ẹrọ ohun elo ati imọ-ẹrọ ile-iṣẹ.
Wọn dayato illa ti firmness, gbona aabo, ati resistance kemikali jẹ ki o ṣee ṣe fun iṣẹ ṣiṣe igbẹkẹle ni diẹ ninu awọn eto mimu omi ti o nbeere julọ.
Bi awọn ilana iṣowo titari si aapọn nla, finer resistance, ati Elo to gun ojutu akoko, alumina seramiki tesiwaju lati ṣeto awọn ami fun to lagbara, ga-konge sisan Iṣakoso irinše.
5. Olutaja
Alumina Technology Co., Ltd., Ltd idojukọ lori iwadi ati idagbasoke, isejade ati tita ti aluminiomu oxide lulú, aluminiomu ohun elo afẹfẹ, aluminiomu ohun elo afẹfẹ crucible, ati be be lo., sìn awọn ẹrọ itanna, amọ, kemikali ati awọn ile-iṣẹ miiran. Niwon awọn oniwe-idasile ni 2005, Ile-iṣẹ naa ti ṣe adehun lati pese awọn alabara pẹlu awọn ọja ati iṣẹ ti o dara julọ. Ti o ba n wa didara ga aluminiomu al2o3, jọwọ lero free lati kan si wa. ([email protected])